Influence of boron- and barium-containing modifiers on the structure of low-chromium cast iron

Influence of boron- and barium-containing modifiers on the structure of
low-chromium cast iron
D.R. Aubakirov
A.Z. Issagulov
A.A. Akberdin
Sv.S. Kvon
V.Yu. Kulikov
S.K. Arinova
A.M. Dostaeva
Ye.P. Chsherbakova
B.B. Sarkenov
A.K. Narembekovа

The paper presents the results of studying the effect of modifying low-chromium hypoeutectic cast iron (chromium
content about 1%) with boron- and barium-containing additives on its structure and hardness. The
modification was carried out with carbothermicferroboron (0.08% of weight of the liquid metal); ferrosilicobarium
(0.05% of weight of liquid metal); complex boron barium ferroalloy (0.14% by weight of liquid metal). The
microstructure and properties were compared with a sample of unmodified cast iron of the same composition.
The Thixomet Pro software was used as the main method of the quantitative analysis of the microstructure that
allows quantitative metallographic analyzing with high accuracy and repeatability.
The analysis of the results obtained shows a positive effect of modification on changes in the microstructure. In
all the experimental samples, grinding and more uniform distribution of carbides, as well as transformation of the
carbides morphology from dendritic to compact granular form, take place. Pearlite colonies in the modified cast
iron are characterized by a higher degree of dispersion than in the reference sample. Such changes in the structure
lead to increasing the hardness of the prototypes.